boiler pressure vessel steel plate alloy steel plate steel 

Place of Origin: Tianjin, China (Mainland) 
inquire
Add to My Favorites
HiSupplier Escrow
Share |

Product Detail

Model No.: A514
Width: 1200mm to 4000mm
Standard: En10025
Min Quantity: 20MT
Packageing Details: International standard
Thickness: 4mm to 150mm
Length: 3000mm to 18000mm
Payment: T/T, L/C
Trade terms: FOB,CIF,CFR
Delivery state: TMCP, Q& T, N, AR, CR, A, Q...

High strength low alloy steel plate A514 alloy high strength steel plate high strength steel plate high tensile steel plate

ITEMS
Grade A,%
Grade B,%
Grade C,%
Grade D,%
Grade E,%
Grade F,%
Grade G,%
Maximum Thickness,
in. (mm)
1 1/4
(32:0.)
1 1/4
(32.0.)
1 1/4
(32.0)
1 1/4
(32.0)
16 (152)
14 (10.2)
2 (51.0.)
Carbon
0.15-0.21
0.12-0.21
0.10-0.20
0.13-0.20
0.12-0.20
0.10-0.20
0.15-0.21
Mn
0.80-1.10
0.70-1.00
1.10-1.50
0.40-0.70
0.40-0.70
0.60-1.00
0.8001.10
P, max
0.035
0.035
0.035
0.035
0.035
0.035
0.035
S,max
0.04
0.04
0.04
0.04
0.04
0.04
0.04
Silicon
0.40-0.80
0.20-0.35
0.15-0.30
0.20-0.35
0.20-0.35
0.15-0.35
0.50-0.90
Nickel
...
...
...
...
...
0.70-1.00
...
Chromium
0.50-0.8
0.4-0.65
0.85-1.2
1.4-2.00
0.4-0.65
0.50-0.90
Mo
0.18-0.28
0.15-0.25
0.20-0.30
0.15-0.25
0.40-0.60
0.40-0.60
0.40-0.60
Vanadium
...
0.03-0.08
...
A
A
0.03-0.08
...
Titanium
...
0.01-0.03
...
0.04-0.10
0.04-0.10
...
...
Zirconium
0.05-0.15B
...
...
...
...
...
0.05-0.15B
Copper
...
...
...
0.20-0.40
0.20-0.40
0.15-0.50
...
Boron
0.0025max
0.0005-0.005
0.001-0.005
0.0015-0.005
0.0015-0.005
0.0005-0.006
0.0025-max
ITEMS
Grade J,%
Grade K,%
Grade L,%
Grade M,%
Grade N,%
Grade P,%
Grade Q,%
Maximum Thickness,
in. (mm)
1 1/4 (32)
2 (51.0.)
2 (51.0.)
2 (51.0.)
3/4 (19·0.)
6(152)
6(152)
Carbon
0.12-0.21
0.10-0.20
0.13-0.20
0.12-0.21
0.15-0.21
0.12-0.21
0.14-0.21
Manganese
0.45-0.70
1.1-1.50
0..40.-
0..70.
10..45-
0..70.
0.80-1.10
0.45-0.70
0.95-1.30
Phosphhorus, max
0.035
0.035
0.035
0.035
0.035
0.035
0.035
Sulfur,max
0.04
0.04
0.04
0.04
0.04
0.04
0.04
Silicon
0.20-0.35
0.15-0.30
0.20-0.35
0.20-0.35
0.40-.0.90
0.20-0.35
0.15-0.35
Nickel
...
...
...
1.20-1.50
1.20-1.50
1.20-1.50
Chromium
...
...
1.15-1.65
...
0.50-0.80
0.85-1.20
1.00-1.50
Molybdenum
0.50-0.65
0.45-0.55
0.25-0.40
0.45-0.60
0.25-max
0.45-0.60
0.40-0.60
Vanadium
...
...
A
...
...
...
...
Titanium
...
...
0.04-0.10
...
...
...
...
Zirconium
...
...
...
0.05-0.15
...
...
Copper
...
...
0.20-0.40
...
...
...
...
Boron
0.001-0.005
0.001-0.005
0.0015-0.005
0.001-0.005
0.005-0.0025
0.001-0.005
...
A May be substituted for part or all of. titanium content on a one for one basis
B Zirconium may be replaced by cerium. When cerium is added, the cerium/sulfur ratio should be approximately 1.5 to 1, based upon heat analysis.
TABLE 2 Tensile and Hardness Requirements
NOTE 1-0n plates wider than 24 in. (610 mm), the test specimen shall be taken in the transverse direction.
NOTE 2-Either the full thickness rectangular specimen shown in Fig. 4 of ASTM Methods and Definitions A 370 for
Mechanical Testing of Steel Products;' or the 'h-in. (12.S-mm) diameter specimen shown in Fig. S of Methods A 370 may
be used for plates over '/. to 1'12 in. (19 to 40 mm) in thickness.
Thickness, in.
Ultimate Tensile Strength
,ksi(Mpa)
Yield StrengthA,
min,kis(MPa)
Enlongation in 2in.
or 50mm, B,C,E %
Reducion of AreaBC,
min %
Brinell hardnessD
Number
To '/4, incl
110 to 130 (760 to 895)
100 (690)
18
40E
235 to 293
Over '/4 to 2'12, incl
110 to 130 (760 to 895)
100 (690)
18
40E,50F
...
Over 2'12 to 6, incl
100 to 130 (690 to 895)
90(620)
18
50F
...
A Measured at 0.2 % offset or O.S % extension under load as described in Section 13 of Methods A 370.
B Elongation and reduction of area not required to be determined for floor plates.
c For plates tested in the transverse direction, the elongation minimum percent is reduced by 2 % and the reduction of
area minimum requirement is reduced by S %.
D See Section 7.
E When measured on the Fig. 4 (Methods A 370) l'h-in. (40-mm) wide specimen (see Note 2 above), the elongation is
determined in a 2-in. or SO-mm gage length which includes the fracture and shows the greatest elongation.
F When measured on the Fig. S (Methods A 370) liz-in. (12.5-mm) round specimen (see Note 2 above
bigPhoto
 Mr. Marvin-Z

Tel: 86-22-58626802
Contact to this supplier

Didn't find what you're looking for? Post Buying Lead or contact HiSupplier Customer Service Center  for help!

Related Search

Find more related products in following catalogs on Hisupplier.com

Company Info